Description
A cold galvanizing primer that contains 52% Type I inorganic zinc in the dried paint film. Resists oxidation, and the galvanizing protection continues even if scratched. Can be topcoated for maximum durability. Contains an additive which results in less smoke and electrode wear when welding through it, and cuts faster than 100% zinc rich coatings.
- A cold galvanizing primer that contains 52% Type I inorganic zinc in the dried paint film.
- Resists oxidation, and the galvanizing protection continues even if scratched.
- Can be topcoated for maximum durability.
- Contains an additive which results in less smoke and electrode wear when welding through it, and cuts faster than 100% zinc rich coatings.
- Covers up to 15 square feet
Suggested Uses:
Eliminate corrosion between welded substrates
Effective touch-up for hot dip galvanized surfaces
Metal fabrication
Piping
| Container Size: | 16 OZ |
| Net Fill Wt. OZ: | 15 |
| Net Fill Wt. G: | 425 |
| Prop 65 (cancer): | no |
| Prop 65 (repro): | yes |
Properties:
Coverage Up to 15 square feet
Cleanup Paint or lacquer thinner
Flammability Extremely Flammable
Flash point -4 F
Specific Gravity 0.87
Solids Content 52%
% Zinc in dried paint film 52%
MIR value 0.90, cannot exceed 1.00
HAPs content 17%
Storage Temperature 40-100F
Application Temperature 50-90F
Heat Resistance 350F
Resin System Modified Epoxy
Shelf life Guaranteed for 2 years
Dry Time*:
To touch 5 minutes
To topcoat 20 minutes
*At 72F, 50% humidity,
1.5 mil thickness
**Curing/Recoat time is extended with
multiple coats and excessively thick coats**
Gloss*: Flat, <15*
*as measured on a 60 degree gloss meter
Meets or exceeds the following performance requirements:
ASTM A780
MIL-P-26915C
MIL-P-46105
DOD-P-21035A
SSPC-Paint 20